Specific battery charging using composition 1 (without addition of lithium perchlorate) shows an optimal range of 0.3 – 0.5 mm thickness and 50-55% relative humidity, Likewise, this behavior was observed for specific accumulator capacity. In the case of specific energy and specific power of the battery, the optimal range of thickness and relative humidity was 0.3 mm and 50-55%, respectively. For this biopolymer composition, it is clear that the electrical properties of these accumulators are due to electrochemically synthesized ppy/pTS and ppy/IC. The electrical properties of electrochemical accumulators assembled using cassava starch biopolymers with chemical composition 2 are shown in Figure 2. For the accumulator charging capacity and specific charge, it is necessary to obtain a thickness of biopolymers of 1.3-1.5 mm and a relative humidity of 50-55%. At this point, the effect of introducing lithium perchlorate (1.5 g) could affect the thickness of the cassava